※ DATA SHEET - Alloy Steel - DIN X2CrNiMoN25-7-4 / W-Nr 1.4410 ※
※ MATERIAL CATEGORY: Common alloy steel - Martensitic and
precipitation hardening corrosion resisting steels
2507 Super Duplex Round Bar Specification
| Standards | Designation |
|---|
| ASTM | A 276 |
|---|
| Length | Diameter |
|---|
| 1000-6000mm | 6-200MM |
|---|
| Type | Certification |
|---|
| 2507 Super Duplex Round Bar | ISO 9001:2008 |
|---|
※ PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by
electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic
examination based on the different levels according to the buyers'
requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution treatment / QTMaraging steels are iron-nickel alloys with absence of carbon and
have metals such as molybdenum, cobalt, titanium and aluminum.
The alloys have ultra-high strength, superior toughness
characteristics and weldability. Typically, these alloys are used
in aerospace applications, machinery and tooling and ordnance
components and fasteners.
※ MATERIAL SPECIFICATIONS
DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312, DIN
EN 10088-5(2005)
※ CHEMICAL COMPOSITION (WEIGHT %)C(％): ≤0.030
Si(％): ≤1.00
Mn(％): ≤2.00
P(％)≤: 0.035
S(％)≤: 0.015
Cr(％): 24.0～26.0
Ni(％): 6.00～8.00
Mo(％): 3.00～4.50
Other(％): N 0.20～0.35
※ MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) UNDER ROOM
TEMPERATURE
Condition: solution treatment
σb/MPa: 750~950
σ0.2≥/MPa: 560
δ5≥(％): 16/14
ψ≥(％): 60
Akv≥/J: 90/70
Hardness HBS30: -
※ MECHANICAL PROPERTIES ( FINAL HEAT TREATMENT OR Q/T) ABOVE ROOM
TEMPERATURE
Hot forming temp/℃: 1150 ~ 900Heat treatment temperature and cooling methods|annealing: 600~640
air cooled
Heat treatment temperature and cooling methods|quenching: 950~1050
air/oil cooled
Heat treatment temperature and cooling methods|tempering: 550~620
Condition: heat treatment
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|100:
520
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|200:
500
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|300:
480
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|400:
-
High temperature yield strength σ0.2/MPa≥/MPa,at below temp/℃|500:
-
※ HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures,
including rate of heating, cooling and soaking times will vary due
to several factors such as the shape and size of each component.
Other considerations during the heat treatment process include the
type of furnace, quenching medium and work piece transfer
facilities. Please consult with the heat treatment provider for
whole guidance on heat treatment of stainless steel grades. We are
delighted to help to work with you the special heat treatment based
on your special requirements.※ AVAILABILITY
Black bar /Flat bar / steel strip / square bar
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
※ TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolt and nut
Pressure vessel
※ TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our
resident team of qualified production engineers.
※ INVENTORY - rolled/forged
Round bar: 40mm
Quantity: 250kg
※ PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mmLength: Fixed length or random length or based on the customer's
special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X
L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 -
2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in
coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs
/donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50
to 35 mm.